Semiconductor device, and manufacturing method for same

ABSTRACT

The present invention is directed to a semiconductor device including a semiconductor chip formed with an SiC-IGBT including an SiC semiconductor layer, a first conductive-type collector region formed such that the collector region is exposed on a second surface of the SiC semiconductor layer, a second conductive-type base region formed such that the base region is in contact with the collector region, a first conductive-type channel region formed such that the channel region is in contact with the base region, a second conductive-type emitter region formed such that the emitter region is in contact with the channel region to define a portion of a first surface of the SiC semiconductor layer, a collector electrode connected to the collector region, and an emitter electrode connected to the emitter region, and a MOSFET including a second conductive-type source region electrically connected to the emitter electrode and a second conductive-type drain region electrically connected to the collector electrode, the MOSFET connected in parallel to the SiC-IGBT.

TECHNICAL FIELD

The present invention relates to a semiconductor device including anSiC-IGBT (Insulated Gate Bipolar Semiconductor) and a method formanufacturing the semiconductor device.

BACKGROUND ART

SiC semiconductor devices have recently become the focus of attention,which are mainly used for systems in various power electronics fieldssuch as motor control systems and power conversion systems.

Patent Document 1, for example, discloses a vertical IGBT including ap-type SiC substrate (collector layer), an n-type drift layer formed onthe SiC substrate, a p-type base region formed in an upper portion ofthe drift layer, and an n-type emitter region formed in an upper portionof the base region.

Patent Document 2 discloses a trench-gate type MOSFET including ann⁺-type SiC substrate, an n⁻-type base layer formed on the SiCsubstrate, a p-type body region formed in a surficial portion of thebase layer, an n⁺-type source region formed in a surficial portion ofthe body region, a gate trench penetrating from the surface of the baselayer through the source region and the body region, and a gateelectrode embedded in the gate trench with a gate insulating filmtherebetween.

PRIOR ART DOCUMENTS Patent Documents

-   Patent Document 1: Japanese Unexamined Patent Publication No.    2011-49267-   Patent Document 2: Japanese Unexamined Patent Publication No.    2011-44688-   Patent Document 3: Japanese Unexamined Patent Publication No.    2010-251517-   Patent Document 4: Japanese Unexamined Patent Publication No.    2010-74051

SUMMARY OF THE INVENTION Means for Solving the Problems

The present invention is directed to a semiconductor device including asemiconductor chip formed with an SiC-IGBT (Insulated Gate BipolarSemiconductor) including an SiC semiconductor layer having a firstsurface and a second surface, a first conductive-type collector regionformed such that the collector region is exposed on the second surfaceof the SiC semiconductor layer, a second conductive-type base regionformed closer to the first surface of the SiC semiconductor layer withrespect to the collector region such that the base region is in contactwith the collector region, a first conductive-type channel region formedcloser to the first surface of the SiC semiconductor layer with respectto the base region such that the channel region is in contact with thebase region, a second conductive-type emitter region formed closer tothe first surface of the SiC semiconductor layer with respect to thechannel region such that the emitter region is in contact with thechannel region, the emitter region defining a portion of the firstsurface of the SiC semiconductor layer, a collector electrode formedsuch that the collector electrode is in contact with the second surfaceof the SiC semiconductor layer, the collector electrode connected to thecollector region, and an emitter electrode formed such that the emitterelectrode is in contact with the first surface of the SiC semiconductorlayer, the emitter electrode connected to the emitter region, and aMOSFET (Metal Oxide Semiconductor Field Effect Transistor) connected inparallel to the SiC-IGBT, the MOSFET including a second conductive-typesource region electrically connected to the emitter electrode, and asecond conductive-type drain region electrically connected to thecollector electrode.

In an SiC-IGBT, electrons or holes are injected from the collectorregion to the base region to cause a conductivity modulation in the baseregion, whereby the on-resistance of the base region can be reduced. Forthis reason, even if the base region may have a low impurityconcentration and therefore a high original resistance due to theimpurity concentration to increase the voltage resistance of the IGBT,the on-resistance can be maintained sufficiently low. As a result, theIGBT is more useful as a device for use in a high-voltage range than anSiC-MOSFET.

Meanwhile, since SiC has a pn bather higher than that of Si, a highon-voltage is required to use the SiC-IGBT in a low-current range (e.g.,of 4 A or lower). This is a very high value even in comparison with theSiC-MOSFET. Unlike the IGBT, the SiC-MOSFET, which uses SiC, undergoes alinear increase in the on-current from the initial stage, which is notparticularly disadvantageous in the low-current range. For use in acurrent range of around 1 A, for example, the SiC-MOSFET has anon-voltage of about 0.8 V and the Si-IGBT has an on-voltage of about 1.3V, while the SiC-IGBT has an on-voltage of 3.5 V, that is, there is adifference of about four times.

Hence, in accordance with the semiconductor device according to thepresent invention, the MOSFET is connected in parallel to the SiC-IGBT.This allows a current to flow through the semiconductor device byturning on the SiC-IGBT or the MOSFET. Accordingly, for use in alow-current range, the semiconductor device can be operated with theon-voltage of the MOSFET, whereby the on-voltage in the low-currentrange can be reduced.

In addition, the MOSFET connected to the SiC-IGBT may be an Si-basedMOSFET such as SiC-MOSFET or Si-MOSFET or, alternatively, a GaN-basedMOSFET or a GaAs-based MOSFET. Among these, SiC-MOSFET is preferable. Inthe case of SiC-MOSFET, the SiC-IGBT and the SiC-MOSFET can beintegrated into a single semiconductor chip.

Specifically, in the semiconductor device according to the presentinvention, it is preferable that the MOSFET includes an SiC-MOSFETprovided in the semiconductor chip, the source region be formedutilizing the emitter region of the SiC-IGBT, the drain region be formedadjacent to the collector region of the SiC-IGBT such that the drainregion is selectively exposed on the second surface of the SiCsemiconductor layer, and the collector electrode be collectivelyconnected to the drain region and the collector region.

With the arrangement above, the emitter region, the base region, thechannel region, the emitter electrode, and the collector electrode canbe shared between the SiC-IGBT and the SiC-MOSFET, whereby these devicescan be integrated into a single unit cell. As a result, thesemiconductor device can be reduced in size and thereby the capacitancebetween the devices can be reduced.

In addition, the SiC-IGBT and the SiC-MOSFET may be formed as separateunit cells in the SiC semiconductor layer.

Also, in the semiconductor device according to the present invention, itis preferable that the SiC semiconductor layer includes a secondconductive-type SiC substrate defining the second surface of the SiCsemiconductor layer and selectively formed with a trench from the secondsurface toward the first surface and a second conductive-type SiC baselayer formed on the SiC substrate to serve as the base region definingthe first surface of the SiC semiconductor layer, in which the drainregion be formed utilizing the SiC substrate and the collector region beformed at the bottom surface of the trench.

The semiconductor device according to the present invention with such astructure can be manufactured by, for example, a method formanufacturing a semiconductor device having an SiC-IGBT and anSiC-MOSFET in a single semiconductor chip, the method including thesteps of forming a second conductive-type SiC base layer on a firstsurface of a second conductive-type SiC substrate having the firstsurface and a second surface and defining a drain region of theSiC-MOSFET, selectively etching the second surface of the SiC substrateto form a trench in the SiC substrate, implanting first conductive-typeimpurities into the bottom surface of the trench to form a collectorregion in the bottom surface, selectively implanting firstconductive-type impurities into the surface of the SiC base layer toform a channel region in a surficial portion of the SiC base layer, andselectively implanting second conductive-type impurities into thesurface of the SiC base layer to form an emitter region in a surficialportion of the channel region, the emitter region serving also as asource region of the SiC-MOSFET.

In accordance with the method above, the collector region and the drainregion, which are selectively exposed on the second surface of the SiCsemiconductor layer, can be formed easily utilizing a knownsemiconductor device manufacturing technique including etching of theSiC substrate and impurity implantation into the SiC substrate and theSiC base layer.

The step of forming the trench may also include the step of etchinguntil the SiC base layer is exposed to the trench.

This allows the deepest portion of the trench to reach the interfacebetween the SiC substrate and the SiC base layer. That is, the deepestportion of the trench may be positioned at the interface between the SiCsubstrate and the SiC base layer or may be at a position nearer thefirst surface of the SiC base layer with respect to the interface. Inthis case, the bottom surface and a portion of the side surface of thetrench is to be defined by the SiC base layer, while the rest of theside surface is to be defined by the SiC substrate. Alternatively, thedeepest portion of the trench may be at a position nearer the secondsurface of the SiC substrate with respect to the interface. In thiscase, the bottom surface and the side surface of the trench are to bedefined by the SiC substrate.

Also, in the semiconductor device according to the present invention,the SiC semiconductor layer may include a first conductive-type SiCsubstrate defining the second surface of the SiC semiconductor layer andselectively formed with a trench from the second surface toward thefirst surface and a second conductive-type SiC base layer formed on theSiC substrate to serve as the base region defining the first surface ofthe SiC semiconductor layer, in which it is preferable that thecollector region be formed utilizing the SiC substrate and the drainregion be formed at the bottom surface of the trench.

It is also preferable that a plurality of the trenches be formed in astriped manner.

In the semiconductor device according to the present invention, the SiCsemiconductor layer may include a second conductive-type SiC substratedefining the second surface of the SiC semiconductor layer andselectively formed with a trench from the second surface toward thefirst surface and a second conductive-type SiC base layer formed on theSiC substrate to serve as the base region defining the first surface ofthe SiC semiconductor layer, in which the drain region and the collectorregion may be formed at the bottom surface of the trench in a manneradjacent to each other.

The semiconductor device according to the present invention with such astructure can be manufactured by, for example, a method formanufacturing a semiconductor device having an SiC-IGBT and anSiC-MOSFET in a single semiconductor chip, the method including thesteps of forming a second conductive-type SiC base layer on a firstsurface of a second conductive-type SiC substrate having the firstsurface and a second surface, selectively etching the second surface ofthe SiC substrate to form a trench in the SiC substrate, selectivelyimplanting first conductive-type impurities into the bottom surface ofthe trench to form a collector region in the bottom surface, selectivelyimplanting second conductive-type impurities into the bottom surface ofthe trench to form a drain region in the bottom surface, selectivelyimplanting first conductive-type impurities into the surface of the SiCbase layer to form a channel region in a surficial portion of the SiCbase layer, and selectively implanting second conductive-type impuritiesinto the surface of the SiC base layer to form an emitter region in asurficial portion of the channel region, the emitter region serving alsoas a source region of the SiC-MOSFET.

Also in accordance with the method above, the collector region and thedrain region, which are selectively exposed on the second surface of theSiC semiconductor layer, can be formed easily utilizing a knownsemiconductor device manufacturing technique including etching of theSiC substrate and impurity implantation into the SiC substrate and theSiC base layer.

Further, in the semiconductor device according to the present invention,the SiC semiconductor layer may include an SiC substrate defining thesecond surface of the SiC semiconductor layer and having a firstconductive-type portion and a second conductive-type portion segmentedsuch that the first and second conductive-type portions are exposedseparately on the second surface and a second conductive-type SiC baselayer formed on the SiC substrate to serve as the base region definingthe first surface of the SiC semiconductor layer, in which it ispreferable that the collector region be formed utilizing the firstconductive-type portion of the SiC substrate and the drain region beformed utilizing the second conductive-type portion of the SiCsubstrate.

In this case, it is preferable that a plurality of the firstconductive-type portions and the second conductive-type portions of theSiC substrate be formed alternately in a striped manner.

In such a case of integrating the SiC-IGBT and the SiC-MOSFET into onechip, the collector electrode, which is collectively connected to thedrain region and the collector region, preferably has metal silicide ina portion in contact with the drain region and the collector region.

The metal silicide can bring the collector electrode into ohmic contactwith the SiC, whether the conductive type of the SiC is p-type orn-type.

Also, in the semiconductor device according to the present invention,the base region preferably includes a drift region having a firstimpurity concentration in contact with the channel region and a bufferregion formed such that the buffer region surrounds the collector regionbetween the drift region and the collector region and having a secondimpurity concentration higher than the first impurity concentration.

With the arrangement above, when the SiC-IGBT is in an off-state, thebuffer region can inhibit the extension of the depletion layer generatedat the interface between the channel region and the drift region andthus prevent punch-through. It is therefore possible to design thesemiconductor device as a punch-through type device to thereby achieve alow on-resistance.

It is then preferable that the SiC semiconductor layer includes a secondconductive-type SiC substrate defining the second surface of the SiCsemiconductor layer and a second conductive-type SiC base layer formedon the SiC substrate to serve as the base region defining the firstsurface of the SiC semiconductor layer, and a trench penetrating fromthe second surface of the SiC substrate through the SiC substrate toreach the SiC base layer be selectively formed, in which the drainregion be formed utilizing the SiC substrate, the collector region beformed at the bottom surface of the trench, and the SiC base layerincludes a second conductive-type buffer layer formed such that thebuffer layer surrounds the collector region to serve as the bufferregion and a second conductive-type drift layer formed on the bufferlayer to serve as the drift region.

The SiC semiconductor layer may also include an SiC substrate definingthe second surface of the SiC semiconductor layer and having a firstconductive-type portion and a second conductive-type portion segmentedsuch that the first and second conductive-type portions are exposedseparately on the second surface and a second conductive-type SiC baselayer formed on the SiC substrate to serve as the base region definingthe first surface of the SiC semiconductor layer, in which it ispreferable that the collector region be formed utilizing the firstconductive-type portion of the SiC substrate, the drain region be formedutilizing the second conductive-type portion of the SiC substrate, andthe SiC base layer includes a second conductive-type buffer layer formedon the SiC substrate such that the buffer layer covers the drain regionand the collector region to serve as the buffer region and a secondconductive-type drift layer formed on the buffer layer to serve as thedrift region.

The semiconductor device according to the present invention preferablyfurther includes a pn diode connected in parallel to the SiC-IGBTincluding a first conductive-type region electrically connected to theemitter electrode, a second conductive-type region electricallyconnected to the collector electrode.

IGBTs, in which anodes or cathodes of pn diodes are connected, cannotincorporate a body diode like MOSFETs. It is therefore difficult toconsume a back electromotive force if occurring to the load.

Hence, in accordance with the semiconductor device according to thepresent invention, the pn diode is connected in parallel to theSiC-IGBT. Accordingly, even if a back electromotive force may occur tothe load, the rectification behavior of the pn diode causes a currentdue to the back electromotive force to flow through the load as a refluxcurrent, which can prevent such a high back electromotive force frombeing applied to the SiC-IGBT.

In such a case of integrating the SiC-IGBT and the SiC-MOSFET into onechip, it is also preferable that the pn diode includes a body diodeincorporated in the MOSFET. The body diode may be formed utilizing a pnjunction between the channel region and the base region of the MOSFETprovided in the semiconductor chip.

This also allows the pn diode to be integrated into the same unit cellas the SiC-IGBT and the SiC-MOSFET, whereby the semiconductor device canbe further reduced in size.

The semiconductor device according to the present invention preferablyfurther includes a Schottky barrier diode connected in parallel to theSiC-IGBT including a second conductive-type drift region, an anodeelectrode forming a Schottky junction with the drift region andelectrically connected to the emitter electrode and a cathode electrodein ohmic contact with the drift region electrically connected to thecollector electrode.

With the arrangement above, since the Schottky barrier diode isconnected in parallel to the SiC-IGBT, the recovery time can beshortened, whereby the semiconductor device can achieve fast recovery.

Also, in the semiconductor device according to the present invention,the semiconductor chip may be arranged such that the base regionincludes a base surficial portion exposed on the first surface of theSiC semiconductor layer to define a portion of the first surface and theemitter electrode includes a Schottky joint portion forming a Schottkyjunction with the base surficial portion, in which it is preferable thatthe Schottky barrier diode includes an SiC-Schottky barrier diodeprovided in the semiconductor chip, the drift region be formed utilizingthe base region of the SiC-IGBT, and the anode electrode be formedutilizing the emitter electrode of the SiC-IGBT.

With the arrangement above, the base region, the emitter electrode, andthe collector electrode can be shared between the SiC-IGBT and theSiC-Schottky barrier diode, whereby these devices can be integrated intoa single unit cell. As a result, the semiconductor device can be reducedin size and thereby the capacitance between the devices can be reduced.

The semiconductor device may further include an interlayer insulatingfilm formed on the first surface of the SiC semiconductor layer andformed with a contact hole through which the base surficial portion isexposed, and further a resin package in which the SiC-IGBT, the MOSFET,and the Schottky barrier diode are collectively encapsulated.

Also, in the semiconductor device according to the present invention, itis preferable that the base region be partially exposed on the firstsurface of the SiC semiconductor layer, in which the semiconductor chipincludes a Schottky electrode formed such that the Schottky electrode isin contact with the exposed portion of the base region and a trench dugfrom the first surface of the SiC semiconductor layer at a positionadjacent to a joint portion between the base region and the Schottkyelectrode, the trench having a bottom surface and a side surface.

With the arrangement above, the base region can be shared between theSiC-IGBT and the SiC-Schottky bather diode, whereby these devices can beintegrated into a single unit cell. As a result, the semiconductordevice can be reduced in size and thereby the capacitance between thedevices can be reduced.

Further, since the trench is formed adjacent to the Schottky jointportion, the electric field intensity at the Schottky interface betweenthe base region and the Schottky electrode can be reduced. As a result,the barrier of the Schottky interface can be set low, whereby theSchottky barrier diode can have a low rise voltage.

In this case, the SiC semiconductor layer preferably includes a firstconductive-type electric field relaxing portion selectively formed onthe bottom surface and on an edge portion of the bottom surface of thetrench.

This can reduce the reverse leakage current in the entire semiconductordevice. That is, since the reverse leakage current can be reduced evenif a reverse voltage close to the breakdown voltage may be applied, thevoltage resistance characteristic of the SiC semiconductor can beefficiently utilized.

In this case, the electric field relaxing portion is preferably formedstraddling between the edge portion of the bottom surface of the trenchand the side surface of the trench and, in particular, preferably formedalong the side surface of the trench to the opening end of the trench.

Further, the trench preferably includes a tapered trench with the bottomsurface in a planar profile and the side surface inclined at an anglegreater than 90 degrees with respect to the planar bottom surface.

The tapered trench can further increase the voltage resistance of thesemiconductor device compared to the case where the side wall standsperpendicularly, at 90 degrees, to the bottom wall.

Moreover, the tapered trench leads to an arrangement in which not onlythe bottom surface but also the whole or part of the side surface isopposed to the opening end of the trench. Accordingly, when firstconductive-type impurities are implanted into the SiC semiconductorlayer via the trench, for example, the impurities incident through theopening end into the trench can reliably hit the side surface of thetrench. As a result, the above-described electric field relaxing portioncan be formed easily.

In addition, the tapered trench is a concept including both a trench theside surface of which is entirely inclined at an angle greater than 90degrees with respect to the bottom surface and a trench the side surfaceof which is partially (e.g., the portion defining the edge portion ofthe trench) inclined at an angle greater than 90 degrees with respect tothe bottom surface.

Also, in the semiconductor device according to the present invention, itis preferable that the Schottky electrode be formed such that theSchottky electrode is embedded in the trench and the electric fieldrelaxing portion have a contact portion forming an ohmic junction withthe Schottky electrode at the bottom surface of the trench.

With the arrangement above, the Schottky electrode can form an ohmicjunction with the pn diode having a pn junction between the contactportion (first conductive-type) and the base region (secondconductive-type). The pn diode is provided in parallel to the Schottkybarrier diode (heterojunction diode) having a Schottky junction betweenthe Schottky electrode and the base region. Accordingly, a surge currentcan partially flow through the incorporated pn diode even if the surgecurrent may flow through the semiconductor device. As a result, thesurge current flowing through the Schottky barrier diode can be reducedwhereby thermal destruction of the Schottky barrier diode due to surgecurrent can be prevented.

Further, in the semiconductor device according to the present invention,it is preferable that the base region includes a base drift regionhaving a first impurity concentration and a low-resistance drift regionformed on the base drift region and having a second impurityconcentration relatively higher than the first impurity concentration,and the trench be formed such that the deepest portion thereof reachesthe low-resistance drift region.

Since the trench-segmented unit cells segmented by the trench have alimited current flow region (current path), if the portions defining theunit cells in the SiC semiconductor layer have a low impurityconcentration, the unit cells may have a high resistance. Hence, thusforming the trench such that the deepest portion thereof reaches thelow-resistance drift region allows all or part of the unit cells to beformed in the low-resistance drift region. Accordingly, in the portionswhere the low-resistance drift region is formed, even if the currentpath may be narrowed, the low-resistance drift region, which has therelatively high second impurity concentration, can suppress an increasein resistance. As a result, the unit cells can have a low resistance.

The first impurity concentration of the base drift region may decreasefrom the second surface to the first surface of the SiC semiconductorlayer. Further, the second impurity concentration of the low-resistancedrift region may be constant from the second surface to the firstsurface of the SiC semiconductor layer or may decrease from the secondsurface to the first surface of the SiC semiconductor layer.

Also, in the semiconductor device according to the present invention,the base region preferably further includes a surficial drift regionformed on the low-resistance drift region and having a third impurityconcentration relatively lower than the second impurity concentration.

With this arrangement, since the impurity concentration in the vicinityof the surface of the SiC semiconductor layer (base region) can be madelow, the electric field intensity at the surface of the SiCsemiconductor layer upon reverse voltage application can be reduced. Asa result, the reverse leakage current can be further reduced.

The SiC-IGBT may include a planar-gate type IGBT including a gateinsulating film formed on the first surface of the SiC semiconductorlayer and a gate electrode formed on the gate insulating film such thatthe gate electrode is opposed to the channel region with the gateinsulating film therebetween or may include a trench-gate type IGBTincluding a gate trench penetrating from the first surface of the SiCsemiconductor layer through the emitter region and the channel region toreach the base region, a gate insulating film formed on the innersurface of the gate trench, and a gate electrode formed on the inside ofthe gate insulating film in the gate trench.

The semiconductor device manufacturing method according to the presentinvention preferably further includes, a step of implanting secondconductive-type impurities into the vicinity of the first surface of theSiC substrate before the step of forming the SiC base layer.

With this method, during etching from the second surface to the firstsurface of the SiC substrate to form a trench, when the etching facereaches the end (near the first surface) of the SiC substrate, anothertype of plasma can be detected different from that during etching of theother portions of the SiC substrate. As a result, the depth of theetching can be controlled precisely.

Also, in the semiconductor device manufacturing method according to thepresent invention, it is preferable that the step of forming the SiCbase layer includes the steps of forming a first high-concentrationimpurity layer on the first surface of the SiC substrate and forming adrift layer on the first high-concentration impurity layer so as to havean impurity concentration relatively lower than that of the firsthigh-concentration impurity layer and the step of forming the trenchincludes the step of selectively forming a trench penetrating throughthe SiC substrate and the high-concentration impurity layer to reach thedrift layer, the method further including, before the step of formingthe collector region, the step of implanting second conductive-typeimpurities into the bottom surface of the trench to form a secondhigh-concentration impurity layer in the bottom surface to thereby forma buffer layer in which the second high-concentration impurity layer andthe first high-concentration impurity layer are integrated.

With the method above, the semiconductor device can be manufacturedhaving an arrangement in which the collector region is surrounded by thebuffer layer.

Furthermore, the semiconductor device according to the present inventioncan be manufactured by a method for manufacturing a semiconductor devicehaving an SiC-IGBT and an SiC-MOSFET in a single semiconductor chip. Themethod may include the steps of forming a second conductive-type SiCbase layer on a first surface of a substrate having the first surfaceand a second surface, removing the substrate to expose a second surfaceof the SiC base layer, selectively implanting first conductive-typeimpurities into the second surface of the SiC base layer to form acollector region in the second surface, selectively implanting secondconductive-type impurities into the second surface of the SiC base layerto form a drain region in the second surface, selectively implantingfirst conductive-type impurities into a first surface of the SiC baselayer to form a channel region in a surficial portion of the SiC baselayer, and selectively implanting second conductive-type impurities intothe first surface of the SiC base layer to form an emitter region in asurficial portion of the channel region, the emitter region serving alsoas a source region of the SiC-MOSFET.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is an external perspective view of a semiconductor packageaccording to a first preferred embodiment of the present invention.

FIG. 2 is a circuit diagram inside the semiconductor chip shown in FIG.1.

FIG. 3 is a schematic cross-sectional view of the semiconductor chipshown in FIG. 1.

FIG. 4A shows a step of a process for manufacturing the semiconductorchip shown in FIG. 3.

FIG. 4B shows a step following that shown in FIG. 4A.

FIG. 4C shows a step following that shown in FIG. 4B.

FIG. 4D shows a step following that shown in FIG. 4C.

FIG. 4E shows a step following that shown in FIG. 4D.

FIG. 4F shows a step following that shown in FIG. 4E.

FIG. 5 shows a first exemplary variation of the trench shown in FIG. 3.

FIG. 6 shows a second exemplary variation of the trench shown in FIG. 3.

FIG. 7 shows an exemplary variation of the gate electrode shown in FIG.3.

FIG. 8 is a circuit diagram of an inverter circuit with thesemiconductor chip shown in FIG. 3 incorporated therein.

FIG. 9 is a schematic cross-sectional view of a semiconductor chipaccording to a second preferred embodiment of the present invention.

FIG. 10A shows a step of a process for manufacturing the semiconductorchip shown in FIG. 9.

FIG. 10B shows a step following that shown in FIG. 10A.

FIG. 10C shows a step following that shown in FIG. 10B.

FIG. 10D shows a step following that shown in FIG. 10C.

FIG. 10E shows a step following that shown in FIG. 10D.

FIG. 10F shows a step following that shown in FIG. 10E.

FIG. 10G shows a step following that shown in FIG. 10F.

FIG. 10H shows a step following that shown in FIG. 10G.

FIG. 11 is a schematic cross-sectional view of a semiconductor chip (ofan SiC substrate segmented type) according to a third preferredembodiment of the present invention.

FIG. 12 is a schematic cross-sectional view of a semiconductor chip (ofan SiC substrate segmented type) according to a fourth preferredembodiment of the present invention.

FIG. 13 is a schematic cross-sectional view of a semiconductor chip (ofa trench-gate type) according to a fifth preferred embodiment of thepresent invention.

FIG. 14 is a schematic cross-sectional view of a semiconductor chip (ofa device separated type) according to a sixth preferred embodiment ofthe present invention.

FIG. 15 is a schematic plan view of a semiconductor chip according to aseventh preferred embodiment of the present invention.

FIG. 16 is a schematic bottom view of the semiconductor chip shown inFIG. 15.

FIG. 17 shows an exemplary variation about the stripe direction of thecollector region shown in FIG. 16.

FIG. 18 is a schematic cross-sectional view of the semiconductor chipaccording to the seventh preferred embodiment of the present invention.

FIG. 19 illustrates the impurity concentration of the SiC substrate andthe SiC base layer.

FIG. 20A shows a step of a process for manufacturing the semiconductorchip shown in FIG. 18.

FIG. 20B shows a step following that shown in FIG. 20A.

FIG. 20C shows a step following that shown in FIG. 20B.

FIG. 20D shows a step following that shown in FIG. 20C.

FIG. 21 is a schematic cross-sectional view of a semiconductor chipaccording to an eighth preferred embodiment of the present invention.

FIG. 22A shows a step of a process for manufacturing the semiconductorchip shown in FIG. 21.

FIG. 22B shows a step following that shown in FIG. 22A.

FIG. 22C shows a step following that shown in FIG. 22B.

FIG. 22D shows a step following that shown in FIG. 22C.

FIG. 23 is a schematic cross-sectional view of a semiconductor chipaccording to a ninth preferred embodiment of the present invention.

FIG. 24A shows a step of a process for manufacturing the semiconductorchip shown in FIG. 23.

FIG. 24B shows a step following that shown in FIG. 24A.

FIG. 24C shows a step following that shown in FIG. 24B.

FIG. 24D shows a step following that shown in FIG. 24C.

FIG. 24E shows a step following that shown in FIG. 24D.

FIG. 24F shows a step following that shown in FIG. 24E.

MODES FOR CARRYING OUT THE INVENTION

Preferred embodiments of the present invention will hereinafter bedescribed in detail with reference to the accompanying drawings.

FIG. 1 is an external perspective view of a semiconductor package 1according to a first preferred embodiment of the present invention. FIG.2 is a circuit diagram inside the semiconductor chip 8 shown in FIG. 1.

The semiconductor package 1, which serves as a semiconductor device,includes a flattened rectangular parallelepiped resin package 2, a gateterminal 3 (G), an emitter terminal 4 (E), and a collector terminal 5(C) encapsulated in the resin package 2.

The three terminals 3 to 5 are each formed of a metal plate in apredetermined shape. In this preferred embodiment, the collectorterminal 5 is formed in a shape including a square island 6 and anelongated rectangular terminal portion 7 extending linearly from a sideof the island 6. The gate terminal 3 and the emitter terminal 4 areformed in approximately the same shape as the terminal portion 7 of thecollector terminal 5 and disposed parallel with each other on one andthe other sides of the terminal portion 7 of the collector terminal 5 ina manner sandwiching the terminal portion 7 of the collector terminal 5.

The semiconductor chip 8 is placed on the collector terminal 5 (in acentral portion of the island 6). An IGBT 9 (Insulated Gate BipolarSemiconductor), a MOSFET 11 incorporating a body diode 10 (pn-Di), and aSchottky bather diode 12 (SBD) are mounted on the semiconductor chip 8.That is, the three devices, IGBT 9, MOSFET 11, and Schottky bather diode12, which serve a switching function, are mounted on the singlesemiconductor chip 8, and the semiconductor chip 8 is supported on theisland 6 of the collector terminal 5.

As shown in FIG. 2, the MOSFET 11, the body diode 10, and the Schottkybarrier diode 12 are connected in parallel to the IGBT 9 in thesemiconductor chip 8.

Specifically, the source (S) of the MOSFET 11, the anode (A) of the bodydiode 10, and the anode (A) of the Schottky barrier diode 12 arerespectively connected to the emitter (E) of the IGBT 9. The drain (D)of the MOSFET 11, the cathode (K) of the body diode 10, and the cathode(K) of the Schottky bather diode 12 are respectively connected to thecollector (C) of the IGBT 9. The gate (G) of the MOSFET 11 is connectedto the gate (G) of the IGBT 9.

The gate (G) of the IGBT 9 is connected to the gate terminal 3 using abonding wire 13, and the emitter (E) of the IGBT 9 is connected to theemitter terminal 4 using a bonding wire 14. The collector (C) of theIGBT 9 is connected to the island 6 of the collector terminal 5.

The resin package 2 then encapsulates the semiconductor chip 8, thebonding wires 13 and 14, the whole of the island 6 and a portion of theterminal portion 7 of the collector terminal 5, a portion of the gateterminal 3, and a portion of the emitter terminal 4. The rest of theterminal portion 7 of the collector terminal 5, the gate terminal 3, andthe emitter terminal 4 are exposed through a side surface of the resinpackage 2.

In addition, the IGBT 9, the MOSFET 11 incorporating the body diode 10,and the Schottky barrier diode 12 may be integrated into thesemiconductor chip 8 (single chip) indicated by the solid line in FIG. 1(i.e., exist on the same chip) or may be provided separately as an IGBTchip 15, a MOSFET chip 16 (incorporating the body diode 10), and aSchottky bather diode chip 17 indicated by the broken line in FIG. 1 aslong as it is capable of configuring the circuit shown in FIG. 2.

In the latter case, the MOSFET 11, the body diode 10, and the Schottkybarrier diode 12 can be connected in parallel to the IGBT 9, as shown inFIG. 2, by connecting the collector (C) of the IGBT chip 15, the drain(D) of the MOSFET chip 16, and the cathode (K) of the Schottky barrierdiode chip 17 to the island 6 of the collector terminal 5, connectingthe emitter (E) of the IGBT chip 15, the source (S) of the MOSFET chip16, and the anode (A) of the Schottky barrier diode chip 17 to theemitter terminal 4 using bonding wires 18 to 20 respectively, andconnecting the gate (G) of the IGBT chip 15 and the gate (G) of theMOSFET chip 16 to the gate terminal 3 using bonding wires 21 and 22respectively.

<Specific Configuration of the Semiconductor Chip 8 (Device IntegratedType)>

FIG. 3 is a schematic cross-sectional view of the semiconductor chip 8shown in FIG. 1.

The semiconductor chip 8 includes an SiC (silicon carbide) semiconductorlayer having a first surface 24 and a second surface 25, an emitterelectrode 26 connected to the first surface 24 of the SiC semiconductorlayer 23, and a collector electrode 27 connected to the second surface25 of the SiC semiconductor layer 23, and is supported on the collectorterminal 5 by bonding the collector electrode 27 and the collectorterminal 5 (island 6) with the emitter electrode 26 being directedupward. The bonding wire 14 shown in FIG. 1 is connected to the emitterelectrode 26.

In the SiC semiconductor layer 23, multiple impurity regionsconstituting the IGBT 9, the MOSFET 11, and the Schottky barrier diode12 are formed and sandwiched vertically between the emitter electrode 26and the collector electrode 27. The emitter electrode 26 and thecollector electrode 27 are shared among the IGBT 9, the MOSFET 11, andthe Schottky barrier diode 12. That is, the emitter electrode 26 and thecollector electrode 27 are external electrodes common to the IGBT 9, theMOSFET 11, and the Schottky bather diode 12. In the MOSFET 11, theemitter electrode 26 serves as a source electrode 28 and the collectorelectrode 27 serves as a drain electrode 29. On the other hand, in theSchottky barrier diode 12, the emitter electrode 26 serves as an anodeelectrode 30 and the collector electrode 27 serves as a cathodeelectrode 31. Accordingly, the SiC-IGBT 9, the SiC-MOSFET 11, and theSiC-Schottky bather diode 12, which are constituted by multiple SiCimpurity regions, are connected in parallel between the emitterelectrode 26 and the collector electrode 27.

The SiC semiconductor layer 23 includes an n⁺-type SiC substrate 32(with a concentration of, for example, 1.0×10¹⁹ to 1.0×10²¹ atoms·cm⁻³;the same applies hereinafter) defining the second surface 25 of the SiCsemiconductor layer 23 and an n⁻-type SiC base layer 33 (SiC epitaxiallayer) (with a concentration of, for example, 5.0×10¹⁶ to 1.0×10¹⁴atoms·cm³; the same applies hereinafter) formed on the SiC substrate 32and defining the first surface 24 of the SiC semiconductor layer 23.

In this preferred embodiment, the n⁺-type SiC substrate 32 defines adrain region 34 of the MOSFET 11 and a cathode region 35 of the Schottkybather diode 12. Also, the SiC base layer 33 serves as a drift region inthe MOSFET 11 and the Schottky bather diode 12. In addition, the n-typeimpurity may be, for example, N (nitrogen), P (phosphorous), or As(arsenic).

In the SiC semiconductor layer 23, multiple trenches 36 are formed thatreach from the second surface 25 to the SiC base layer 33. The multipletrenches 36 are formed in, for example, a striped manner at regularintervals. In addition, the trenches 36 may be formed in, for example, agrid manner without limiting to the striped manner.

The side surface of each trench 36 is defined by the SiC substrate 32,while the bottom surface is defined by the SiC base layer 33. P⁺-typecollector regions 37 (collector regions 37 of the IGBT 9) (with aconcentration of, for example, 1.0×10¹⁸ to 1.0×10²⁰ atoms·cm⁻³; the sameapplies hereinafter) are formed on the bottom surface (second surfaceportion of the SiC base layer 33). In addition, the p-type impurity maybe, for example, B (boron) or Al (aluminum).

The pitch between adjacent trenches 36 (trench pitch P) is preferably 1μm to 500 μm. With this range of the trench pitch P, the portionsbetween adjacent collector regions 37 (i.e., the portions where thecurrent paths of the MOSFET 11 are formed) can be prevented from beingclosed by the depletion layer extending from the interface between thecollector regions 37 and the SiC base layer 33.

The collector electrode 27 penetrates collectively into all the trenches36 so as to cover the second surface 25 of the SiC substrate 32, and isconnected to the SiC substrate 32 via the side surface of each trench36, while connected to the collector regions 37 via the bottom surfacesof the respective trenches 36. The collector electrode 27 is an AlCu(alloy of aluminum and copper) electrode with a metal silicide 38 (e.g.,nickel (Ni) silicide or titanium (Ti) silicide) formed in a mannercontacting the inner surface (side surface and bottom surface) of eachtrench 36. This can bring the collector electrode 27 into ohmic contactwith any target of whichever conductive type including the n⁺-type SiCsubstrate 32 and the p⁺-type collector regions 37.

Multiple well-like p-type channel regions 39 (with a concentration of,for example, 1×10¹⁶ to 1×10¹⁹ atoms·cm⁻³; the same applies hereinafter)are selectively formed in surficial portions of the SiC base layer 33.The multiple channel regions 39 are exposed on the first surface 24 ofthe SiC base layer 33 to define portions of the first surface 24. On theother hand, between the multiple channel regions 39, the SiC base layer33 is partially exposed on the first surface 24 as a base surficialportion 40.

An n⁺-type emitter region 41 (emitter region 41 of the IGBT 9) is formedin a portion of the first surface 24 of each channel region 39. Theemitter region 41 is exposed on the first surface 24 of the SiC baselayer 33 to define a portion of the first surface 24. The emitter region41 serves also as a source region 42 of the MOSFET 11.

In a central portion of each channel region 39, a p⁺-type channelcontact region 43 is formed that penetrates from the first surface 24 ofthe SiC base layer 33 through the emitter region 41 to reach the channelregion 39.

A gate insulating film 44 composed of silicon oxide (SiO₂) is formed onthe first surface 24 of the SiC base layer 33, and a gate electrode 45composed of polysilicon is formed on the gate insulating film 44. Thegate electrode 45 is opposed to the channel region 39, which is exposedon the first surface 24 of the SiC base layer 33, with the gateinsulating film 44 straddling between the emitter region 41 and the basesurficial portion 40.

An interlayer insulating film 46 composed of SiO₂ is layered on the SiCbase layer 33 in a manner covering the gate electrode 45.

The interlayer insulating film 46 is formed with contact holes 47 and 48penetrating through the interlayer insulating film 46 in the thicknessdirection directly above the emitter region 41 and the base surficialportion 40 respectively.

The emitter electrode 26 penetrates collectively into the contact holes47 and 48 in a manner covering the interlayer insulating film 46 and isconnected to the emitter region 41, the channel contact region 43, andthe base surficial portion 40 through the contact holes 47 and 48. Theemitter electrode 26 is an AlCu electrode. Accordingly, the emitterelectrode 26 includes an ohmic contact portion 49 in ohmic contact withthe n⁺-type emitter region 41 and the p⁺-type channel contact region 43,which have a high impurity concentration, and a Schottky joint portion50 forming a Schottky junction with the n⁻-type SiC base layer 33, whichhas a low impurity concentration.

As described heretofore, the semiconductor chip 8 is formed with thevertical IGBT 9 including the emitter electrode 26, the emitter region41 connected to the emitter electrode 26, the channel region 39 formedin a manner contacting the side of the emitter region 41 nearer thesecond surface 25 of the SiC semiconductor layer 23, the SiC base layer33 formed in a manner contacting the side of the channel region 39nearer the second surface 25 of the SiC semiconductor layer 23, thecollector regions 37 formed in a manner contacting the side of the SiCbase layer 33 nearer the second surface 25 of the SiC semiconductorlayer 23, and the collector electrode 27 connected to the collectorregions 37.

The emitter electrode 26 and the collector electrode 27 of the IGBT 9are then shared between the MOSFET 11 and the Schottky barrier diode 12,and the MOSFET 11 also includes the emitter region 41 (source region42), the channel region 39, the SiC base layer 33, and the SiC substrate32 as impurity regions connected to these electrodes. The Schottkybarrier diode 12 also includes the SiC base layer 33 and the SiCsubstrate 32 as impurity regions connected to the electrodes 26 and 27.

That is, in the semiconductor chip 8, the IGBT 9, the MOSFET 11, and theSchottky barrier diode 12 are integrated into a single unit cell.

The MOSFET 11 incorporates a pn diode (body diode 10) defined by a pnjunction between the p-type channel region 39 and the n⁻-type SiC baselayer 33, where the p-side (anode side) of the body diode 10 isconnected with the anode electrode 30 and the emitter electrode 26,while the n-side (cathode side) is connected with the cathode electrode31 and the collector electrode 27.

Thus, the three devices, IGBT 9, MOSFET 11 incorporating the body diode10, and Schottky bather diode 12, are collectively mounted on thesemiconductor chip 8 and connected in parallel to each other.

<Method for Manufacturing the Semiconductor Chip 8 (Device IntegratedType)>

FIGS. 4A to 4F show sequential steps of a process for manufacturing thesemiconductor chip 8 shown in FIG. 3.

In order to manufacture the semiconductor chip 8, an epitaxial growthmethod such as CVD (Chemical Vapor Deposition), LPE (Liquid PhaseEpitaxy), or MBE (Molecular Beam Epitaxy) is used to grow an SiC crystalwhile doping n-type impurities into a surface of the wafer SiC substrate32 as shown in FIG. 4A. This causes the n⁻-type SiC base layer 33 to beformed on the SiC substrate 32.

Next, as shown in FIG. 4B, a hard mask 51 is formed and patterned on thesecond surface 25 of the SiC substrate 32 and then dry-etched at leastuntil the SiC base layer 33 is exposed on the second surface 25 of theSiC substrate 32. This causes the SiC substrate 32 to be selectively dugfrom the second surface 25 and thereby the trenches 36 to be formed.

Next, as shown in FIG. 4C, with the hard mask 51 used to form thetrenches 36 being left, p-type impurities are accelerated toward thetrenches 36 exposed through the hard mask 51 to be implanted into thebottom surfaces of the trenches 36 (ion implantation). Next, the SiCbase layer 33 is annealed. This causes the p-type impurities implantedinto the bottom surfaces of the trenches 36 to be activated and therebythe collector regions 37 to be formed in the SiC base layer 33.Thereafter, the hard mask 51 is peeled off.

Next, as shown in FIG. 4D, hard mask formation and ion implantation areconducted according to the shapes of the channel region 39, the emitterregion 41, and the channel contact region 43 as well as the types ofimpurities, and then the SiC base layer 33 is annealed in a similarmanner as in the step shown in FIG. 4C. This causes the n-typeimpurities and the p-type impurities implanted into the SiC base layer33 to be activated and thereby the channel region 39, the emitter region41, and the channel contact region 43 to be simultaneously formed in theSiC base layer 33.

Next, as shown in FIG. 4E, a thermal oxidation method, for example, isused to form the gate insulating film 44 on the first surface 24 of theSiC base layer 33. Subsequently, a CVD technique, for example, is usedto deposit polysilicon over the SiC base layer 33. The depositedpolysilicon is then patterned to form the gate electrode 45.

Next, a CVD method, for example, is used to layer the interlayerinsulating film 46 on the SiC base layer 33. Subsequently, theinterlayer insulating film 46 and the gate insulating film 44 areselectively dry-etched to form the contact holes 47 and 48simultaneously.

Next, as shown in FIG. 4F, a sputtering method, for example, is used todeposit AlCu on the interlayer insulating film 46 in a manner fillingthe contact holes 47 and 48. This causes the emitter electrode 26 to beformed. Thereafter, the metal silicide 38 is formed on the innersurfaces of the trenches 36, and then a sputtering method, for example,is used to deposit AlCu on the second surface 25 of the SiC substrate 32in a manner filling the inside of the metal silicide 38. This causes thecollector electrode 27 to be formed.

The semiconductor chip 8 shown in FIG. 3 is thus formed through theforegoing steps.

In the IGBT 9 mounted on the semiconductor package 1, holes are injectedfrom the p⁺-type collector regions 37 to the n⁻-type SiC base layer 33to cause a conductivity modulation in the SiC base layer 33, whereby theon-resistance of the SiC base layer 33 (drift layer) can be reduced. Forthis reason, even if the SiC base layer 33 may have a low impurityconcentration and/or an increased thickness and therefore a highoriginal resistance to increase the voltage resistance of the IGBT 9,the on-resistance can be maintained sufficiently low. As a result, theIGBT 9 is more useful as a device for use in a high-voltage range thanan SiC-MOSFET.

Meanwhile, since SiC has a pn bather higher than that of Si, a highon-voltage is required to use the IGBT in a low-current range (e.g., of4 A or lower). This is a very high value even in comparison with theSiC-MOSFET. Unlike the IGBT, the SiC-MOSFET, which uses SiC, undergoes alinear increase in the on-current from the initial stage, which is notparticularly disadvantageous in the low-current range. For use in acurrent range of around 1 A, for example, the SiC-MOSFET has anon-voltage of about 0.8 V and the Si-IGBT has an on-voltage of about 1.3V, while the SiC-IGBT has an on-voltage of 3.5 V, that is, there is adifference of about four times.

Hence, in accordance with the semiconductor package 1, the MOSFET 11 isconnected in parallel to the IGBT 9. This allows a current to flowthrough the semiconductor package 1 by turning on the IGBT 9 or theMOSFET 11. Accordingly, for use in a low-current range, thesemiconductor package 1 can be operated with the on-voltage of theMOSFET 11, whereby the on-voltage in the low-current range can bereduced.

Also, in this preferred embodiment, the IGBT 9, the MOSFET 11incorporating the body diode 10, and the Schottky bather diode 12 areintegrated into a single unit cell in the semiconductor chip 8. As aresult, the semiconductor package 1 can be reduced in size and therebythe capacitance between the devices can be reduced.

On the other hand, the IGBT 9, in which the cathode of the pn diodedefined by the pn junction between the p-type channel region 39 and then⁻-type SiC base layer 33 is connected to the cathode of the pn diodedefined by the pn junction between the p⁺-type collector regions 37 andthe n⁻-type SiC base layer 33, cannot incorporate a body diode 10 likethe MOSFET 11. It is therefore difficult to consume a back electromotiveforce if occurring to the load.

Hence, in accordance with the semiconductor package 1, the MOSFET 11incorporates the body diode 10 and the body diode 10 is connected inparallel to the IGBT 9. Accordingly, even if a back electromotive forcemay occur to the load, the rectification behavior of the body diode 10causes a current due to the back electromotive force to flow through theload as a reflux current, which can prevent such a high backelectromotive force from being applied to the IGBT 9.

Further, since the Schottky barrier diode 12 is connected in parallel tothe IGBT 9, the recovery time can be shortened, whereby thesemiconductor package 1 can achieve fast recovery.

In addition, since the IGBT 9 and the MOSFET 11 are integrated into thesame semiconductor chip 8, the collector regions 37 and the drain region34, which are selectively exposed on the second surface 25 of the SiCsemiconductor layer 23, can be formed utilizing a known semiconductordevice manufacturing technique including etching of the SiC substrate 32and impurity implantation into the SiC base layer 33 as shown in FIG. 4Ato 4C. The collector regions 37 and the drain region 34 can thus beformed easily at the second surface 25 of the SiC semiconductor layer23.

In addition, the deepest portions of the trenches 36 are not required tobe positioned at the interface between the SiC substrate 32 and the SiCbase layer 33 as shown in FIG. 3, but may be, for example, at a positionnearer the first surface 24 of the SiC base layer 33 with respect to theinterface as shown in FIG. 5. In this case, the bottom surface and aportion of the side surface of each trench 36 is to be defined by theSiC base layer 33, while the rest of the side surface is to be definedby the SiC substrate 32. Alternatively, the deepest portions may be at aposition nearer the second surface 25 of the SiC substrate 32 withrespect to the interface as shown in FIG. 6. In this case, the bottomsurface and the side surface of each trench 36 are to be defined by theSiC substrate 32.

Further, the gate electrode 45 may be formed straddling between adjacentchannel regions 39 in a manner covering the base surficial portion 40 asshown in FIG. 7, for example. In this case, since the base surficialportion 40 is not exposed and cannot be connected with the emitterelectrode 26 (Schottky joint portion 50), the Schottky bather diode 12is not to be provided.

Furthermore, the IGBT 9, the MOSFET 11, and the Schottky bather diode 12may be formed as separate unit cells in the SiC semiconductor layer 23.

The semiconductor package 1 may be built and used in an inverter circuitas shown in FIG. 8, for example. In addition, in FIG. 8, the IGBT 9 andthe MOSFET 11 are integrated into a single transistor for the purpose ofeasy illustration.

The inverter circuit 58 is a three-phase inverter circuit connected to athree-phase motor 59, including a DC power supply 60 and a switchingportion 61.

A high-voltage wire 62 and a low-voltage wire 63 are connected,respectively, to the high-voltage and low-voltage sides of the DC powersupply 60.

The switching portion 61 includes three series circuits 64 to 66corresponding, respectively, to the U-phase 59U, V-phase 59V, andW-phase 59W of the three-phase motor 59.

The series circuits 64 to 66 are connected in parallel between thehigh-voltage wire 62 and the low-voltage wire 63. The series circuits 64to 66 include high-side transistors (IGBT 9+MOSFET 11) 67H to 69H on thehigh-voltage side and low-side transistors (IGBT 9+MOSFET 11) 67L to 69Lon the low-voltage side respectively. Regenerative diodes 70H to 72H and70L to 72L are connected in parallel to the respective transistors 67Hto 69H and 67L to 69L such that the forward current flows from thelow-voltage side to the high-voltage side.

A switching signal is input from a control circuit not shown to thegates of the transistors 67H to 69H and 67L to 69L. In response to theswitching signal, the transistors 67H to 69H and 67L to 69L performswitching operations. This causes a three-phase AC current to flowthrough the three-phase motor 59 and drive the three-phase motor 59.

<Semiconductor Package 1 According to a Second Preferred Embodiment>

FIG. 9 is a schematic cross-sectional view of a semiconductor chipaccording to a second preferred embodiment of the present invention. InFIG. 9, portions corresponding to those shown in FIG. 3 are designatedby the same reference signs to omit the description thereof.

In the semiconductor chip 71 shown in FIG. 9, the multiple trenches 36are formed in a manner penetrating through the SiC substrate 32 into theSiC base layer 33. This causes a step 72 to be provided between thebottom surface of each trench 36 and the second surface of the SiC baselayer 33. The second surface of the SiC base layer 33 selectivelyprotrudes correspondingly to the steps 72 to form convex portions 73.

The SiC base layer 33 includes an n⁺-type buffer layer 74 formed in amanner surrounding the collector regions 37 and an n⁻-type drift layer75 formed on the buffer layer 74 to define the first surface 24 of theSiC semiconductor layer 23. The impurity concentration of the bufferlayer 74 is higher than that of the drift layer 75. For example, thebuffer layer 74 has an impurity concentration of 1.0×10¹⁸ to 1.0×10¹⁵atoms·cm⁻³, while the drift layer 75 has an impurity concentration of5.0×10¹⁶ to 1.0×10¹⁴ atoms·cm⁻³.

The buffer layer 74 includes first portions 76 protruding toward thesecond surface 25 of the SiC semiconductor layer 23 along the surfacesof the convex portions 73 and second portions 77 protruding in theopposite direction of the first portions 76 to surround the collectorregions 37, the first and second portions formed in a switchback manneralternately according to the pitch P of the trenches 36.

The drift layer 75 constitutes a major portion of the SiC base layer 33and is in contact with the channel region 39 at the first surface 24 ofthe SiC semiconductor layer 23.

A high-concentration impurity region 78 having an impurity concentrationhigher than that of the other portions of the SiC substrate 32 is formedin the vicinity of the first surface of the SiC substrate 32 (in thevicinity of the bottom of each trench 36). The high-concentrationimpurity region 78 is in contact with each convex portion 73 of the SiCbase layer 33.

FIGS. 10A to 10H show sequential steps of a process for manufacturingthe semiconductor chip shown in FIG. 9.

In order to manufacture the semiconductor chip 71, n-type impurities(e.g., P or As) are implanted into a surface of the wafer SiC substrate32 to form the high-concentration impurity region 78 as shown in FIG.10A.

Next, as shown in FIG. 10B, an epitaxial growth method such as CVD, LPE,or MBE is used to grow an SiC crystal while doping n-type impuritiesinto the surface of the SiC substrate 32. This causes a firsthigh-concentration impurity layer 79 as a base of the buffer layer 74and the drift layer 75 to be formed in this order and thereby then⁻-type SiC base layer 33 to be formed on the SiC substrate 32.

Next, as shown in FIG. 10C, hard mask formation and ion implantation areconducted according to the shapes of the channel region 39, the emitterregion 41, and the channel contact region 43 as well as the types ofimpurities. This causes the channel region 39, the emitter region 41,and the channel contact region 43 to be simultaneously formed in the SiCbase layer 33.

Next, as shown in FIG. 10D, a hard mask 51 is formed and patterned onthe second surface 25 of the SiC substrate 32 and then dry-etched atleast until the drift layer 75 is exposed through the firsthigh-concentration impurity layer 79 on the second surface 25 of the SiCsubstrate 32. This causes the SiC substrate 32 to be selectively dugfrom the second surface 25 and thereby the trenches 36 to be formed.

During this time, since the high-concentration impurity region 78 isformed in the vicinity of the first surface of the SiC substrate 32,when the etching face reaches the end (near the first surface) of theSiC substrate 32, another type of plasma can be detected different fromthat during etching of the other portions of the SiC substrate 32. As aresult, the depth of the etching can be controlled precisely so as topenetrate through the first high-concentration impurity layer 79 to theextent possible.

Next, as shown in FIG. 10E, with the hard mask 51 used to form thetrenches 36 being left, n-type impurities are accelerated toward thetrenches 36 exposed through the hard mask 51 to be implanted into thebottom surfaces of the trenches 36. This causes a secondhigh-concentration impurity layer 80 and the first high-concentrationimpurity layer 79 to be integrated and thereby the buffer layer 74 to beformed.

Next, as shown in FIG. 10F, p-type impurities are accelerated toward thetrenches 36 exposed through the hard mask 51 to be implanted into thebottom surfaces of the trenches 36 (second portions 77 of the bufferlayer 74). This causes the collector regions 37 to be formed in the SiCbase layer 33. Thereafter, the hard mask 51 is peeled off and then theSiC base layer 33 is annealed. This causes the channel region 39, theemitter region 41, the channel contact region 43, the buffer layer 74,the n-type impurities and the p-type impurities implanted into thecollector regions 37 to be activated.

Next, as shown in FIG. 10G, a thermal oxidation method, for example, isused to form the gate insulating film 44 on the first surface 24 of theSiC base layer 33. Subsequently, a CVD method, for example, is used todeposit polysilicon over the SiC base layer 33. The depositedpolysilicon is then patterned to form the gate electrode 45.

Next, a CVD method, for example, is used to layer the interlayerinsulating film 46 on the SiC base layer 33. Subsequently, theinterlayer insulating film 46 and the gate insulating film 44 areselectively dry-etched to form the contact holes 47 and 48simultaneously.

Next, as shown in FIG. 10H, a sputtering method, for example, is used todeposit AlCu on the interlayer insulating film 46 in a manner fillingthe contact holes 47 and 48. This causes the emitter electrode 26 to beformed. Thereafter, the metal silicide 38 is formed on the innersurfaces of the trenches 36, and then a sputtering method, for example,is used to deposit AlCu on the second surface 25 of the SiC substrate 32in a manner filling the inside of the metal silicide 38. This causes thecollector electrode 27 to be formed.

The semiconductor chip 71 shown in FIG. 9 is thus formed through theforegoing steps.

As described heretofore, the semiconductor chip 71 can also achieve thesame operational advantages as the above-described semiconductor chip 8.

Further, in the semiconductor chip 71 with the buffer layer 74 formedtherein, when the IGBT 9 is in an off-state, the buffer layer 74 caninhibit the extension of the depletion layer generated at the interfacebetween the channel region 39 and the drift layer 75 and thus preventpunch-through. It is therefore possible to design the semiconductor chip71 as a punch-through type device to thereby achieve a lowon-resistance.

The semiconductor package 1 according to the present invention may alsobe embodied as shown in FIGS. 11 to 14. In addition, in FIGS. 11 to 14,portions corresponding to those shown in FIGS. 1 to 3 are designated bythe same reference signs. The detailed description of the portionsdesignated by the same reference signs will be omitted below.

(1) SiC Substrate Segmented Type (FIGS. 11 and 12)

For example, the SiC substrate 52 may be segmented into multipleportions such that p⁺-type portions 53 and n⁺-type portions 54 arearranged alternately in a striped manner and exposed on the secondsurface 25 of the SiC substrate 52 so that the p⁺-type portions 53 canbe utilized as the collector regions 37 of the IGBT 9, while the n⁺-typeportions 54 can be utilized as the drain region 34 of MOSFET 11.

Also in this SiC substrate segmented type, the SiC base layer 33 mayhave a bilayer structure including the buffer layer 74 and the driftlayer 75 as shown in FIG. 12. In this case, the buffer layer 74 isformed in a manner covering the p⁺-type portions 53 and the n⁺-typeportions 54 collectively along the first surface of the SiC substrate32.

(2) Trench-Gate Type (FIG. 13)

The IGBT 9 may be, for example, a trench-gate type, although it is aplanar-gate type in the above-described preferred embodiments.

In the trench-gate type IGBT 9, a gate trench 55 is formed in a centralportion of the channel region 39, the gate trench 55 penetrating fromthe first surface 24 of the SiC base layer 33 through the emitter region41 and the channel region 39 to reach the SiC base layer 33 at thedeepest portion.

A gate insulating film 56 composed of SiO₂ is formed in a mannercovering the entire inner surface of the gate trench 55. The inside ofthe gate insulating film 56 is then filled with polysilicon, so that agate electrode 57 is embedded in the gate trench 55.

The channel contact region 43 is formed in a peripheral portionsurrounding the central portion of the channel region 39 in a mannerpenetrating from the first surface 24 of the SiC base layer 33 through aperipheral portion of the emitter region 41 to reach the channel region39.

(3) Device Separated Type (FIG. 14)

The IGBT 9, the MOSFET 11, and the Schottky barrier diode 12 may beformed separately and respectively as an IGBT chip 15, a MOSFET chip 16,and a Schottky bather diode chip 17, although they are integrated intothe same semiconductor chip 8 in the above-described preferredembodiments.

In this case, the MOSFET chip 16 and the Schottky bather diode chip 17may be formed using not SiC but another semiconductor material such asSi, GaN, or GaAs.

The semiconductor chip according to the present invention may also beimplemented in the following seventh to ninth preferred embodiments.

FIG. 15 is a schematic plan view of a semiconductor chip 101 accordingto a seventh preferred embodiment of the present invention. FIG. 16 is aschematic bottom view of the semiconductor chip 101 shown in FIG. 15.FIG. 17 shows an exemplary variation about the stripe direction of thecollector region 109 shown in FIG. 16. FIG. 18 is a schematiccross-sectional view of the semiconductor chip 101 according to theseventh preferred embodiment of the present invention.

The semiconductor chip 101 has, for example, a square chip shape in aplan view. The chip-shaped semiconductor chip 101 has vertical andhorizontal lengths of several millimeters on the paper surfaces of FIGS.15 and 16.

The semiconductor chip 101 includes an n⁺-type SiC substrate 102 and ann⁻-type SiC base layer 103 formed on the SiC substrate 102. The n⁺-typeSiC substrate 102 defines a drain region 104 of the MOSFET 11 and acathode region 105 of the Schottky barrier diode 12. The SiC base layer103 serves as a drift region 116 in the MOSFET 11 and the Schottkybarrier diode 12.

Multiple second surface trenches 106 are formed in a manner penetratingfrom the second surface of the SiC substrate 102 through the SiCsubstrate 102 into the SiC base layer 103. This causes a step 107 to beprovided between the bottom surface of each second surface trench 106and the second surface of the SiC base layer 103. The second surface ofthe SiC base layer 103 selectively protrudes correspondingly to thesteps 107 to form convex portions 108.

The multiple second surface trenches 106 are formed in, for example, astriped manner at regular intervals. In addition, the trenches may beformed in, for example, a grid manner without limiting to the stripedmanner. In the case of a striped manner, the stripe direction may beparallel with the direction of first surface trenches 131 (to bedescribed hereinafter) as shown in FIG. 16 or may intersect with thedirection of the first surface trenches 131 (to be describedhereinafter) as shown in FIG. 17.

The side surface of each second surface trench 106 is defined by the SiCsubstrate 102, while the bottom surface is defined by the SiC base layer103. P⁺-type collector regions 109 (collector regions 109 of the IGBT 9)are formed on the bottom surface (second surface portion of the SiC baselayer 103).

A collector electrode 110 is then formed in a manner covering the entiresecond surface of the SiC substrate 102. The collector electrode 110penetrates collectively into all the second surface trenches 106 and isconnected to the SiC substrate 102 via the side surface of each secondsurface trench 106, while connected to the collector regions 109 via thebottom surfaces of the respective second surface trenches 106. Thecollector electrode 110 is an AlCu electrode with a metal silicide 111formed in a manner contacting the inner surface (side surface and bottomsurface) of each second surface trench 106. This can bring the collectorelectrode 110 into ohmic contact with any target of whichever conductivetype including the n⁺-type SiC substrate 102 and the p⁺-type collectorregions 109.

The collector electrode 110 is an external electrode common to the IGBT9, the MOSFET 11, and the Schottky bather diode 12. In the MOSFET 11,the collector electrode 110 serves as a drain electrode 112. On theother hand, in the Schottky barrier diode 12, the collector electrode110 serves as a cathode electrode 113.

A high-concentration impurity region 114 having an impurityconcentration higher than that of the other portions of the SiCsubstrate 102 is formed in the vicinity of the first surface of the SiCsubstrate 102 (in the vicinity of the bottom of each second surfacetrench 106). The high-concentration impurity region 114 is in contactwith each convex portion 108 of the SiC base layer 103.

The SiC base layer 103 includes a buffer region 115 and a drift region116.

The buffer region 115 includes first portions 117 protruding toward thesecond surface of the SiC base layer 103 along the surfaces of theconvex portions 108 and second portions 118 protruding in the oppositedirection of the first portions 117 to surround the collector regions109, the first and second portions formed in a switchback manneralternately according to the pitch of the second surface trenches 106.

The drift region 116 has a trilayer structure including a base driftregion 125, a low-resistance drift region 126, and a surficial driftregion 127, where the base drift region 125 is in contact with thebuffer region 115 and the surficial drift region 127 is exposed on thefirst surface of the SiC base layer 103.

A P-type channel region 119 is selectively formed in a surficial portionof the drift region 116, and an n⁺-type emitter region 120 is formed ina surficial portion of the channel region 119. The emitter region 120 isexposed on the first surface of the SiC base layer 103 to define aportion of the first surface. The emitter region 120 serves also as asource region 121 of the MOSFET 11.

The emitter region 120 and the channel region 119 constitute a unit cellof the IGBT 9 (MOSFET 11). Between adjacent unit cells of the IGBT 9(MOSFET 11), the drift region 116 is partially exposed on the firstsurface of the SiC base layer 103.

A gate trench 122 is formed in the SiC base layer 103, the gate trenchpenetrating from the first surface of the SiC base layer 103 through theemitter region 120 and the channel region 119 to reach an intermediateportion of the low-resistance drift region 126 at the deepest portion.This causes the emitter region 120 (source region 121) to define aportion of the side surface of the gate trench 122. The channel region119 similarly defines a portion of the side surface of the gate trench122. The drift region 116 defines a portion of the side surface and thebottom surface of the gate trench 122.

A gate insulating film 123 composed of an insulator such as SiO₂ isformed in a manner covering the entire inner surface (side surface andbottom surface) of the gate trench 122. A gate electrode 124 composed ofa conductor such as polysilicon is then embedded in the gate trench 122.The gate electrode 124 is opposed to the emitter region 120 (sourceregion 121), the channel region 119, and the drift region 116 via thegate insulating film 123.

A field insulating film 128 composed of an insulator such as SiO₂ isformed on the first surface of the SiC base layer 103. The fieldinsulating film 128 has a contact hole through which the SiC base layer103 is partially exposed as an active region 129 and covers a fieldregion 130 that surrounds the active region 129.

Between adjacent unit cells of the IGBT 9 (MOSFET 11) in the activeregion 129, a first surface trench 131 is formed penetrating from thefirst surface of the SiC base layer 103 through the surficial driftregion 127 to reach an intermediate portion of the low-resistance driftregion 126 at the deepest portion. The first surface trench 131 isformed to have the same depth and shape as the gate trench 122.

The gate trench 122 and the first surface trench 131 may be formed in astriped manner parallel with (see FIG. 16) or intersecting with (e.g.,perpendicular to) (see FIG. 17) the direction of the second surfacetrenches 106.

The gate trench 122 and the first surface trench 131 are defined by abottom surface parallel with the first surface of the SiC base layer 103and a side surface inclined with respect to the bottom surface. Theinclination angle θ of the side surface is, for example, 90 degrees to135 degrees. The depth of the first surface trench 131 (distance fromthe first surface of the SiC base layer 103 to the bottom surface of thefirst surface trench 131) is, for example, 3000 Å to 15000 Å. The widthof the first surface trench 131 perpendicular to the longitudinaldirection (at the deepest portion) is 0.3 μm to 10 μm.

The specific shape of the gate trench 122 and the first surface trench131 may be a U-shaped trench having an inclination angle θ of about 90degrees and a U-shaped bottom portion in a cross-sectional view, inwhich the edge portion of the bottom surface is curved outward so thatthe side surface and the bottom surface are connected via the curvedsurface as exemplified in FIG. 18, however, it is not limited thereto,the side surface and the bottom surface may be connected via an angularsurface, for example.

The gate trench 122 and the first surface trench 131 may also be formedin, for example, an inverted trapezoidal trench having an inclinationangle θ of greater than 90 degrees in a cross-sectional view taken alongthe width direction perpendicular to the longitudinal direction. In theinverted trapezoidal trench, the side surface may be entirely inclinedat an inclination angle θ of greater than 90 degrees or a portion (lowerportion) of the side surface may be selectively inclined at aninclination angle θ of greater than 90 degrees, while the other portions(upper portion) of the side surface may be formed at 90 degrees withrespect to the bottom surface.

On the bottom surface and the side surface of the first surface trench131, a p-type layer 132 serving as an electric field relaxing portion isformed along the inner surface of the first surface trench 131. Thep-type layer 132 is formed from the bottom surface of the first surfacetrench 131 through the edge portion to the opening end of the firstsurface trench 131 in a manner covering both the channel region 119 andthe emitter region 120 (source region 121).

The p-type layer 132 also forms a pn junction with the n-type SiC baselayer 103. This causes the Schottky barrier diode 12 to be connected inparallel to the pn diode 133 constituted by the p-type layer 132 and then-type SiC base layer 103 (low-resistance drift region 126).

In the p-type layer 132, a p⁺-type contact layer 134 is formed on aportion of the bottom surface of the first surface trench 131. Thecontact layer 134 is formed linearly in the longitudinal direction ofthe first surface trench 131 and has a depth (e.g., 0.05 μm to 0.2 μm)from the bottom surface of the first surface trench 131 to anintermediate portion of the p-type layer 132 in the depth direction.

On the other hand, an annular trench 135 penetrating from the firstsurface of the field region 130 through the surficial drift region 127to reach an intermediate portion of the low-resistance drift region 126at the deepest portion is formed in the field region 130. The annulartrench 135 is formed in a manner surrounding the active region 129.

On the bottom surface and the side surface of the annular trench 135, aguard ring 136 is formed along the inner surface of the annular trench135 in a manner exposed on the inner surface. The guard ring 136 isformed in the same step as the p-type layer 132 and has the sameimpurity concentration and thickness as the p-type layer 132.

An emitter electrode 137 composed of AlCu is formed on the fieldinsulating film 128. The emitter electrode 137 is connected to theemitter region 120 (source region 121), the surficial drift region 127,and the contact layer 134 within the contact hole of the fieldinsulating film 128.

That is, the emitter electrode 137 is an external electrode common tothe IGBT 9, the MOSFET 11, and the Schottky barrier diode 12. In theMOSFET 11, the emitter electrode 137 serves as a source electrode 138.On the other hand, in the Schottky barrier diode 12, the emitterelectrode 137 serves as an anode electrode 139.

Accordingly, the emitter electrode 137 includes an ohmic contact portion140 in ohmic contact with the n⁺-type emitter region 120 and the p⁺-typecontact layer 134, which have a high impurity concentration, and aSchottky joint portion 141 forming a Schottky junction with the n⁻-typesurficial drift region 127, which has a low impurity concentration.

A surface protection film 142 composed of an insulator such as SiN isformed on the uppermost surface of the semiconductor chip 101. In acentral portion of the surface protection film 142, an opening is formedthrough which the emitter electrode 137 is exposed. The bonding wire 14shown in FIG. 1 is bonded to the emitter electrode 137 through theopening.

As described heretofore, the semiconductor chip 101 is formed with thevertical IGBT 9 including the emitter electrode 137, the emitter region120 connected to the emitter electrode 137, the channel region 119formed in a manner contacting the side of the emitter region 120 nearerthe second surface of the SiC base layer 103, the drift region 116formed in a manner contacting the side of the channel region 119 nearerthe second surface of the SiC base layer 103, the collector region 109formed in a manner contacting the side of the drift region 116 nearerthe second surface of the SiC base layer 103, and the collectorelectrode 110 connected to the collector region 109.

The emitter electrode 137 and the collector electrode 110 of the IGBT 9are then shared between the MOSFET 11 and the Schottky bather diode 12,and the MOSFET 11 also includes the emitter region 120 (source region121), the channel region 119, the drift region 116, and the drain region104 as impurity regions connected to these electrodes. The Schottkybarrier diode 12 also includes the drift region 116 and the cathoderegion 105 as impurity regions connected to these electrodes.

That is, in the semiconductor chip 101, the IGBT 9, the MOSFET 11, andthe Schottky barrier diode 12 are integrated into a single unit cell.

Thus, the three devices, IGBT 9, MOSFET 11, and Schottky barrier diode12, are collectively mounted on the semiconductor chip 101 and connectedin parallel to each other.

<Impurity Concentration of the SiC Base Layer 103>

Next, the impurity concentration of the SiC substrate 102 and the SiCbase layer 103 will be described with reference to FIG. 19.

FIG. 19 illustrates the impurity concentration of the SiC substrate 102and the SiC base layer 103.

As shown in FIG. 19, the SiC substrate 102 and the SiC base layer 103are each composed of n-type SiC containing n-type impurities. Thesesatisfy the magnitude relationship of the impurity concentration: SiCsubstrate 102>buffer region 115>drift region 116.

The SiC substrate 102 has an approximately constant concentration of,for example, 5×10¹⁸ to 5×10¹⁹ cm⁻³ in the thickness direction. Thebuffer region 115 has a constant concentration or a concentrationreduced along the surface of, for example, 1×10¹⁷ to 5×10¹⁸ cm⁻³ in thethickness direction.

The concentration of the drift region 116 shows stepwise changes at theinterfaces of the base drift region 125, the low-resistance drift region126, and the surficial drift region 127. That is, with respect to eachinterface, there is a concentration difference between the layer nearerthe first surface and the layer nearer the second surface.

The base drift region 125 has a constant concentration of, for example,5×10¹⁴ to 5×10¹⁶ cm⁻³ in the thickness direction. In addition, theconcentration of the base drift region 125 may decrease from about3×10¹⁶ cm⁻³ to about 5×10¹⁵ cm⁻³ continuously from the second surfacetoward the first surface of the SiC base layer 103 as indicated by thebroken line in FIG. 19.

The low-resistance drift region 126 has a constant concentration higherthan that of the base drift region 125, for example, 5×10¹⁵ to 5×10¹⁷cm⁻³ in the thickness direction. In addition, the concentration of thelow-resistance drift region 126 may decrease from about 3×10¹⁷ cm⁻³ toabout 1×10¹⁶ cm⁻³ continuously from the second surface toward the firstsurface of the SiC base layer 103 as indicated by the broken line inFIG. 19.

The surficial drift region 127 has a constant concentration lower thanthat of the base drift region 125 and the low-resistance drift region126, for example, 5×10¹⁴ to 1×10¹⁶ cm⁻³ in the thickness direction.

As shown in FIG. 18, since the Schottky barrier diode 12, which has astripe-like unit cell (line cell) sandwiched between adjacent firstsurface trenches 131, has a current flow region (current path) limitedby the distance between the adjacent first surface trenches 131, if theportions defining the unit cell in the SiC base layer 103 have a lowimpurity concentration, the unit cell may have a high resistance.

Hence, as shown in FIG. 19, the concentration of the low-resistancedrift region 126 defining the base portion of the unit cell is sethigher than that of the base drift region 125. Accordingly, even if thecurrent path may be limited by the distance between the first surfacetrenches 131, the low-resistance drift region 126, which has therelatively high concentration, can suppress an increase in resistance ofthe unit cell. As a result, the unit cell can have a low resistance.

On the other hand, since the surficial drift region 127, which has therelatively low concentration, is provided in a surficial portion of theunit cell in contact with the emitter electrode 137 (anode electrode139), the electric field intensity at the surface of the SiC base layer103 upon reverse voltage application can be reduced. As a result, thereverse leakage current can be further reduced.

Next, a process for manufacturing the semiconductor chip 101 shown inFIG. 18 will be described.

FIGS. 20A to 20D show sequential steps of the process for manufacturingthe semiconductor chip 101 shown in FIG. 18.

First, as shown in FIG. 20A, in accordance with the steps shown in FIGS.10A and 10B, the high-concentration impurity region 114 is formed on asurface of the wafer SiC substrate 102, and then a firsthigh-concentration impurity region 143 as a base of the buffer region115 and the drift region 116 are epitaxially grown sequentially to formthe n⁻-type SiC base layer 103.

Next, as shown in FIG. 20B, in accordance with the step shown in FIG.10C, hard mask formation and ion implantation are conducted according tothe shapes of the channel region 119 and the emitter region 120 (sourceregion 121) as well as the types of impurities. This causes the channelregion 119 and the emitter region 120 (source region 121) to be formedin the SiC base layer 103.

Next, a hard mask is formed according to the patterns of the gate trench122, the first surface trench 131, and the annular trench 135 and then,through etching using the hard mask, the gate trench 122, the firstsurface trench 131, and the annular trench 135 are simultaneously formedto have the same depth.

Next, impurities are selectively implanted into the inner surfaces ofthe first surface trench 131 and the annular trench 135 to form thep-type layer 132 and the guard ring 136 simultaneously. Further,impurities are selectively formed on the bottom surface of the firstsurface trench 131 to form the contact layer 134.

Next, as shown in FIG. 20C, in accordance with the step shown in FIG.10D, a hard mask is formed and patterned on the second surface of theSiC substrate 102 and then dry-etched at least until the drift region116 (base drift region 125) is exposed through the firsthigh-concentration impurity region 143 on the second surface of the SiCsubstrate 102. This causes the SiC substrate 102 to be selectively dugfrom the second surface and thereby the second surface trenches 106 tobe formed.

Next, as shown in FIG. 20D, in accordance with the step shown in FIG.10E, n-type impurities are implanted into the bottom surfaces of thesecond surface trenches 106 to form the buffer region 115. Next, inaccordance with the step shown in FIG. 10F, p-type impurities areimplanted into the bottom surfaces of the second surface trenches 106(second portions 118 of the buffer region 115) to form the collectorregions 109 in the SiC base layer 103.

Thereafter, the SiC base layer 103 is annealed. This causes the n-typeimpurities and the p-type impurities implanted into the drift region116, the channel region 119, the emitter region 120 (source region 121),the contact layer 134, the buffer region 115, and the collector regions109 to be activated.

Subsequently, in accordance with the above-described method or a knownsemiconductor manufacturing technique, the gate insulating film 123, thegate electrode 124, the field insulating film 128, the emitter electrode137, the collector electrode 110, etc., are formed to obtain thesemiconductor chip 101 shown in FIG. 18.

As described heretofore, the semiconductor chip 101 can also achieve thesame operational advantages as the above-described semiconductor chips 8and 71.

Further, in accordance with the semiconductor chip 101, since the firstsurface trench 131 is formed adjacent to the Schottky joint portion 141,the electric field intensity at the Schottky interface between the SiCbase layer 103 and the anode electrode 139 can be reduced. As a result,the barrier of the Schottky interface can be set low, whereby theSchottky bather diode can have a low rise voltage.

Furthermore, since the p-type layer 132 is formed on the inner surfaceof the first surface trench 131, the reverse leakage current can bereduced in the entire semiconductor chip 101. That is, since the reverseleakage current can be reduced even if a reverse voltage close to thebreakdown voltage may be applied, the voltage resistance characteristicof the SiC semiconductor can be efficiently utilized.

In addition, since the pn diode 133 is connected in parallel to theSchottky barrier diode 12, a surge current, if it may flow through thesemiconductor chip 101, can partially flow through the incorporated pndiode 133. As a result, the surge current flowing through the Schottkybarrier diode 12 can be reduced whereby thermal destruction of theSchottky barrier diode 12 due to surge current can be prevented.

Next, a semiconductor chip 151 according to an eighth preferredembodiment will be described.

FIG. 21 is a schematic cross-sectional view of the semiconductor chip151 according to the eighth preferred embodiment of the presentinvention. In FIG. 21, portions corresponding to those shown in FIG. 18are designated by the same reference signs to omit the descriptionthereof.

In the semiconductor chip 101 according to the above-described seventhpreferred embodiment, the multiple second surface trenches 106 areformed and disposed in a striped manner in the active region 129. On theother hand, in the semiconductor chip 151 according to the eighthpreferred embodiment, a single second surface trench 152 is formedcorrespondingly to the multiple first surface trenches 131 formed in astriped manner. The second surface trench 152 is formed in the secondsurface of the SiC substrate 102 in a manner covering approximately theentire active region 129.

Drain regions 153 of the MOSFET 11 (cathode regions 154 of the Schottkybarrier diode 12) and collector regions 155 of the IGBT 9 are formedalternately in a striped manner on the bottom surface of the secondsurface trench 152.

FIGS. 22A to 22D show sequential steps of a process for manufacturingthe semiconductor chip 151 shown in FIG. 21.

First, as shown in FIG. 22A, in accordance with the step shown in FIG.20A, the high-concentration impurity region 114 is formed on a surfaceof the wafer SiC substrate 102, and then a first high-concentrationimpurity region 143 as a base of the buffer region 115 and the driftregion 116 are epitaxially grown sequentially to form the n⁻-type SiCbase layer 103.

Next, as shown in FIG. 22B, in accordance with the step shown in FIG.20B, hard mask formation and ion implantation are conducted according tothe shapes of the channel region 119 and the emitter region 120 (sourceregion 121) as well as the types of impurities. This causes the channelregion 119 and the emitter region 120 (source region 121) to be formedin the SiC base layer 103.

Next, a hard mask is formed according to the patterns of the gate trench122, the first surface trench 131, and the annular trench 135 and then,through etching using the hard mask, the gate trench 122, the firstsurface trench 131, and the annular trench 135 are simultaneously formedto have the same depth.

Next, impurities are selectively implanted into the inner surfaces ofthe first surface trench 131 and the annular trench 135 to form thep-type layer 132 and the guard ring 136 simultaneously. Further,impurities are selectively formed on the bottom surface of the firstsurface trench 131 to form the contact layer 134.

Next, as shown in FIG. 22C, in accordance with the step shown in FIG.20C, a hard mask is formed and patterned on the second surface of theSiC substrate 102 and then dry-etched at least until the drift region116 (base drift region 125) is exposed through the firsthigh-concentration impurity region 143 on the second surface of the SiCsubstrate 102. This causes the SiC substrate 102 to be selectively dugfrom the second surface and thereby the second surface trench 152 to beformed.

Next, as shown in FIG. 22D, in accordance with the step shown in FIG.20D, n-type impurities are implanted into the bottom surface of thesecond surface trench 152 to form the buffer region 115. Next, p-typeimpurities are implanted into the bottom surface of the second surfacetrench 152 to form the collector regions 155 in the SiC base layer 103.Further, n-type impurities are implanted into the bottom surface of thesecond surface trench 152 to form the drain regions 153 (cathode regions154) in the SiC base layer 103.

Thereafter, the SiC base layer 103 is annealed. This causes the n-typeimpurities and the p-type impurities implanted into the drift region116, the channel region 119, the emitter region 120 (source region 121),the contact layer 134, the buffer region 115, the collector regions 155,and the drain regions 153 (cathode regions 154) to be activated.

Subsequently, in accordance with the above-described method or a knownsemiconductor manufacturing technique, the gate insulating film 123, thegate electrode 124, the field insulating film 128, the emitter electrode137, the collector electrode 110, etc., are formed to obtain thesemiconductor chip 151 shown in FIG. 21.

As described heretofore, the semiconductor chip 151 can also achieve thesame operational advantages as the above-described semiconductor chips8, 71, and 101.

Next, a semiconductor chip 161 according to a ninth preferred embodimentwill be described.

FIG. 23 is a schematic cross-sectional view of the semiconductor chip161 according to the ninth preferred embodiment of the presentinvention. In FIG. 23, portions corresponding to those shown in FIG. 18are designated by the same reference signs to omit the descriptionthereof.

In the semiconductor chips 101 and 151 according to the above-describedseventh and eighth preferred embodiments, the SiC substrate 102 isprovided to support the SiC base layer 103 thereon. On the other hand,in the semiconductor chip 161 according to the ninth preferredembodiment, the SiC substrate 102 is not provided, so that the entiresecond surface of the SiC base layer 103 is exposed.

A buffer region 162 is formed over the entire second surface of theexposed SiC base layer 103. In the buffer region 162, drain regions 163of the MOSFET 11 (cathode regions 164 of the Schottky barrier diode 12)and collector regions 165 of the IGBT 9 are formed alternately in astriped manner so as to be exposed on the second surface of the SiC baselayer 103.

FIGS. 24A to 24F show sequential steps of a process for manufacturingthe semiconductor chip 161 shown in FIG. 23.

First, as shown in FIG. 24A, only the base drift region 125 isepitaxially grown on a surface of a wafer substrate 166 to form then⁻-type SiC base layer 103. The substrate 166 used is not limited to anSiC substrate, but may adopt various substrates.

Next, as shown in FIG. 24B, a technique such as grinding, dry etching,or sand blasting is used to grind the substrate 166 until the secondsurface of the SiC base layer 103 is exposed to thereby remove thesubstrate 166.

Next, as shown in FIG. 24C, epitaxial growth or ion implantation is usedto form the low-resistance drift region 126 and the surficial driftregion 127 sequentially on the base drift region 125.

Next, as shown in FIG. 24D, n-type impurities are implanted into theentire second surface of the SiC base layer 103 to form the bufferregion 162.

Next, as shown in FIG. 24E, in accordance with the step shown in FIG.20B, hard mask formation and ion implantation are conducted according tothe shapes of the channel region 119 and the emitter region 120 (sourceregion 121) as well as the types of impurities. This causes the channelregion 119 and the emitter region 120 (source region 121) to be formedin the SiC base layer 103.

Next, a hard mask is formed according to the patterns of the gate trench122, the first surface trench 131, and the annular trench 135 and then,through etching using the hard mask, the gate trench 122, the firstsurface trench 131, and the annular trench 135 are simultaneously formedto have the same depth.

Next, impurities are selectively implanted into the inner surfaces ofthe first surface trench 131 and the annular trench 135 to form thep-type layer 132 and the guard ring 136 simultaneously. Further,impurities are selectively formed on the bottom surface of the firstsurface trench 131 to form the contact layer 134.

Next, as shown in FIG. 24F, in accordance with the step shown in FIG.20D, p-type impurities are implanted into the second surface of the SiCbase layer 103 to form the collector regions 65 in the SiC base layer103. Further, n-type impurities are implanted into the second surface ofthe SiC base layer 103 to form the drain regions 163 (cathode regions164) in the SiC base layer 103.

Thereafter, the SiC base layer 103 is annealed. This causes the n-typeimpurities and the p-type impurities implanted into the drift region116, the channel region 119, the emitter region 120 (source region 121),the contact layer 134, the buffer region 162, the collector regions 165,and the drain regions 163 (cathode regions 164) to be activated.

Subsequently, in accordance with the above-described method or a knownsemiconductor manufacturing technique, the gate insulating film 123, thegate electrode 124, the field insulating film 128, the emitter electrode137, the collector electrode 110, etc., are formed to obtain thesemiconductor chip 161 shown in FIG. 23.

As described heretofore, the semiconductor chip 161 can also achieve thesame operational advantages as the above-described semiconductor chips8, 71, 101, and 151.

Although the preferred embodiments of the present invention haveheretofore been described, the present invention can be embodied instill other forms.

For example, an arrangement may be adopted in which the conductive typeof the semiconductor portions in the IGBT 9, the body diode 10, theMOSFET 11, and the Schottky barrier diode 12 is inverted. In the IGBT 9,for example, the p-type portions may be n-type, while the n-typeportions may be p-type.

In the seventh to ninth preferred embodiments, the unit cells of theIGBT 9 and the MOSFET 11 and the unit cells of the Schottky bather diode12 are arranged alternately. However, the arrangement is notparticularly limited, and two or more of the latter unit cells may bearranged between a pair of the former unit cells, for example.

The features understood from the disclosure of the above-describedpreferred embodiments may also be combined between different preferredembodiments. Further, the components presented in the preferredembodiments may be combined within the scope of the present invention.

The preferred embodiments of the present invention are merely specificexamples used to clarify the technical contents of the presentinvention, and the present invention should not be understood as beinglimited to these specific examples, and the spirit and scope of thepresent invention is to be limited solely by the appended claims.

The present application corresponds to Japanese Patent Application No.2011-169349 filed in the Japan Patent Office on Aug. 2, 2011, JapanesePatent Application No. 2011-234058 filed in the Japan Patent Office onOct. 25, 2011, and Japanese Patent Application No. 2011-273401 filed inthe Japan Patent Office on Dec. 14, 2011, the entire disclosure of whichis incorporated herein by reference.

DESCRIPTION OF SIGNS

-   -   1 Semiconductor package    -   2 Resin package    -   3 Gate terminal    -   4 Emitter terminal    -   5 Collector terminal    -   6 Island (of the collector terminal)    -   7 Terminal portion (of the collector terminal)    -   8 Semiconductor chip    -   9 IGBT    -   10 Body diode    -   11 MOSFET    -   12 Schottky barrier diode    -   13 Bonding wire    -   14 Bonding wire    -   15 IGBT chip    -   16 MOSFET chip    -   17 Schottky barrier diode chip    -   18 Bonding wire    -   19 Bonding wire    -   20 Bonding wire    -   21 Bonding wire    -   22 Bonding wire    -   23 SiC semiconductor layer    -   24 First surface (of the SiC semiconductor layer)    -   25 Second surface (of the SiC semiconductor layer)    -   26 Emitter electrode    -   27 Collector electrode    -   28 Source electrode    -   29 Drain electrode    -   30 Anode electrode    -   31 Cathode electrode    -   32 SiC substrate    -   33 SiC base layer    -   34 Drain region    -   35 Cathode region    -   36 Trench    -   37 Collector region    -   38 Metal silicide    -   39 Channel region    -   40 Base surficial portion    -   41 Emitter region    -   42 Source region    -   43 Channel contact region    -   44 Gate insulating film    -   45 Gate electrode    -   46 Interlayer insulating film    -   47 Contact hole    -   48 Contact hole    -   49 Ohmic contact portion    -   50 Schottky joint portion    -   51 Hard mask    -   52 SiC substrate    -   53 P⁺-type portion    -   54 N⁺-type portion    -   55 Gate trench    -   56 Gate insulating film    -   57 Gate electrode    -   58 Inverter circuit    -   59 Three-phase motor    -   59U U-phase (of the three-phase motor)    -   59V V-phase (of the three-phase motor)    -   59W W-phase (of the three-phase motor)    -   60 DC power supply    -   61 Switching unit    -   62 High-voltage wire    -   63 Low-voltage wire    -   64 Series circuit    -   65 Series circuit    -   66 Series circuit    -   67H High-side transistor    -   67L Low-side transistor    -   68H High-side transistor    -   68L Low-side transistor    -   69H High-side transistor    -   69L Low-side transistor    -   71 Semiconductor chip    -   72 Step    -   73 Convex portion    -   74 Buffer layer    -   75 Drift layer    -   76 First portion (of the buffer layer)    -   77 Second portion (of the buffer layer)    -   78 High-concentration impurity region    -   79 First high-concentration impurity layer    -   80 Second high-concentration impurity layer    -   101 Semiconductor chip    -   102 SiC substrate    -   103 SiC base layer    -   104 Drain region    -   105 Cathode region    -   106 Second surface trench    -   107 Step    -   108 Convex portion    -   109 Collector region    -   110 Collector electrode    -   111 Metal silicide    -   112 Drain electrode    -   113 Cathode electrode    -   114 High-concentration impurity region    -   115 Buffer region    -   116 Drift region    -   117 First portion (of the buffer region)    -   118 Second portion (of the buffer region)    -   119 Channel region    -   120 Emitter region    -   121 Source region    -   122 Gate trench    -   123 Gate insulating film    -   124 Gate electrode    -   125 Base drift region    -   126 Low-resistance drift region    -   127 Surficial drift region    -   128 Field insulating film    -   129 Active region    -   130 Field region    -   131 First surface trench    -   132 P-type layer    -   133 pn diode    -   134 Contact layer    -   135 Annular trench    -   136 Guard ring    -   137 Emitter electrode    -   138 Source electrode    -   139 Anode electrode    -   140 Ohmic contact portion    -   141 Schottky joint portion    -   142 Surface protection film    -   143 First high-concentration impurity region    -   151 Semiconductor chip    -   152 Second surface trench    -   153 Drain region    -   154 Cathode region    -   155 Collector region    -   161 Semiconductor chip    -   162 Buffer region    -   163 Drain region    -   164 Cathode region    -   165 Collector region    -   166 Substrate

The invention claimed is:
 1. A semiconductor device comprising: a semiconductor chip formed with an SiC-IGBT (Insulated Gate Bipolar Semiconductor) including: an SiC semiconductor layer having a first surface and a second surface, a first conductive-type collector region formed such that the collector region is exposed on the second surface of the SiC semiconductor layer, a second conductive-type base region formed closer to the first surface of the SiC semiconductor layer with respect to the collector region such that the base region is in contact with the collector region, a first conductive-type channel region formed closer to the first surface of the SiC semiconductor layer with respect to the base region such that the channel region is in contact with the base region, a second conductive-type emitter region formed closer to the first surface of the SiC semiconductor layer with respect to the channel region such that the emitter region is in contact with the channel region, the emitter region defining a portion of the first surface of the SiC semiconductor layer, a collector electrode formed such that the collector electrode is in contact with the second surface of the SiC semiconductor layer, the collector electrode connected to the collector region, and an emitter electrode formed such that the emitter electrode is in contact with the first surface of the SiC semiconductor layer, the emitter electrode connected to the emitter region; and a MOSFET (Metal Oxide Semiconductor Field Effect Transistor) connected in parallel to the SiC-IGBT, the MOSFET including: a second conductive-type source region electrically connected to the emitter electrode; and a second conductive-type drain region electrically connected to the collector electrode, wherein the MOSFET includes an SiC-MOSFET provided in the semiconductor chip, the source region is formed utilizing the emitter region of the SiC-IGBT, the drain region is formed adjacent to the collector region of the SiC-IGBT such that the drain region is selectively exposed on the second surface of the SiC semiconductor layer, the collector electrode is collectively connected to the drain region and the collector region, the SiC semiconductor layer includes: a second conductive-type SiC substrate defining the second surface of the SiC semiconductor layer and selectively formed with a trench from the second surface toward the first surface, and a second conductive-type SiC base layer formed on the SiC substrate to serve as the base region defining the first surface of the SiC semiconductor layer, wherein the drain region is formed utilizing the SiC substrate, and the collector region is formed at the bottom surface of the trench.
 2. The semiconductor device according to claim 1, wherein a plurality of the trenches are formed in a striped manner.
 3. The semiconductor device according to claim 1, wherein a deepest portion of the trench reaches the interface between the SiC substrate and the SiC base layer.
 4. A semiconductor device comprising: a semiconductor chip formed with an SiC-IGBT (Insulated Gate Bipolar Semiconductor) including: an SiC semiconductor layer having a first surface and a second surface, a first conductive-type collector region formed such that the collector region is exposed on the second surface of the SiC semiconductor layer, a second conductive-type base region formed closer to the first surface of the SiC semiconductor layer with respect to the collector region such that the base region is in contact with the collector region, a first conductive-type channel region formed closer to the first surface of the SiC semiconductor layer with respect to the base region such that the channel region is in contact with the base region, a second conductive-type emitter region formed closer to the first surface of the SiC semiconductor layer with respect to the channel region such that the emitter region is in contact with the channel region, the emitter region defining a portion of the first surface of the SiC semiconductor layer, a collector electrode formed such that the collector electrode is in contact with the second surface of the SiC semiconductor layer, the collector electrode connected to the collector region, and an emitter electrode formed such that the emitter electrode is in contact with the first surface of the SiC semiconductor layer, the emitter electrode connected to the emitter region; and a MOSFET (Metal Oxide Semiconductor Field Effect Transistor) connected in parallel to the SiC-IGBT, the MOSFET including: a second conductive-type source region electrically connected to the emitter electrode; and a second conductive-type drain region electrically connected to the collector electrode, wherein the MOSFET includes an SiC-MOSFET provided in the semiconductor chip, the source region is formed utilizing the emitter region of the SiC-IGBT, the drain region is formed adjacent to the collector region of the SiC-IGBT such that the drain region is selectively exposed on the second surface of the SiC semiconductor layer, the collector electrode is collectively connected to the drain region and the collector region, the SiC semiconductor layer includes: a first conductive-type SiC substrate defining the second surface of the SiC semiconductor layer and selectively formed with a trench from the second surface toward the first surface, and a second conductive-type SiC base layer formed on the SiC substrate to serve as the base region defining the first surface of the SiC semiconductor layer, wherein the collector region is formed utilizing the SiC substrate, and the drain region is formed at the bottom surface of the trench.
 5. A semiconductor device comprising: a semiconductor chip formed with an SiC-IGBT (Insulated Gate Bipolar Semiconductor) including: an SiC semiconductor layer having a first surface and a second surface, a first conductive-type collector region formed such that the collector region is exposed on the second surface of the SiC semiconductor layer, a second conductive-type base region formed closer to the first surface of the SiC semiconductor layer with respect to the collector region such that the base region is in contact with the collector region, a first conductive-type channel region formed closer to the first surface of the SiC semiconductor layer with respect to the base region such that the channel region is in contact with the base region, a second conductive-type emitter region formed closer to the first surface of the SiC semiconductor layer with respect to the channel region such that the emitter region is in contact with the channel region, the emitter region defining a portion of the first surface of the SiC semiconductor layer, a collector electrode formed such that the collector electrode is in contact with the second surface of the SiC semiconductor layer, the collector electrode connected to the collector region, and an emitter electrode formed such that the emitter electrode is in contact with the first surface of the SiC semiconductor layer, the emitter electrode connected to the emitter region; and a MOSFET (Metal Oxide Semiconductor Field Effect Transistor) connected in parallel to the SiC-IGBT, the MOSFET including: a second conductive-type source region electrically connected to the emitter electrode; and a second conductive-type drain region electrically connected to the collector electrode, wherein the MOSFET includes an SiC-MOSFET provided in the semiconductor chip, the source region is formed utilizing the emitter region of the SiC-IGBT, the drain region is formed adjacent to the collector region of the SiC-IGBT such that the drain region is selectively exposed on the second surface of the SiC semiconductor layer, the collector electrode is collectively connected to the drain region and the collector region, the SiC semiconductor layer includes: an SiC substrate defining the second surface of the SiC semiconductor layer and having a first conductive-type portion and a second conductive-type portion segmented such that the first and second conductive-type portions are exposed separately on the second surface, and a second conductive-type SiC base layer formed on the SiC substrate to serve as the base region defining the first surface of the SiC semiconductor layer, wherein the collector region is formed utilizing the first conductive-type portion of the SiC substrate, and the drain region is formed utilizing the second conductive-type portion of the SiC substrate.
 6. The semiconductor device according to claim 5, wherein a plurality of the first conductive-type portions and the second conductive-type portions of the SiC substrate are formed alternately in a striped manner.
 7. A semiconductor device comprising: a semiconductor chip formed with an SiC-IGBT (Insulated Gate Bipolar Semiconductor) including: an SiC semiconductor layer having a first surface and a second surface, a first conductive-type collector region formed such that the collector region is exposed on the second surface of the SiC semiconductor layer, a second conductive-type base region formed closer to the first surface of the SiC semiconductor layer with respect to the collector region such that the base region is in contact with the collector region, a first conductive-type channel region formed closer to the first surface of the SiC semiconductor layer with respect to the base region such that the channel region is in contact with the base region, a second conductive-type emitter region formed closer to the first surface of the SiC semiconductor layer with respect to the channel region such that the emitter region is in contact with the channel region, the emitter region defining a portion of the first surface of the SiC semiconductor layer, a collector electrode formed such that the collector electrode is in contact with the second surface of the SiC semiconductor layer, the collector electrode connected to the collector region, and an emitter electrode formed such that the emitter electrode is in contact with the first surface of the SiC semiconductor layer, the emitter electrode connected to the emitter region; and a MOSFET (Metal Oxide Semiconductor Field Effect Transistor) connected in parallel to the SiC-IGBT, the MOSFET including: a second conductive-type source region electrically connected to the emitter electrode; and a second conductive-type drain region electrically connected to the collector electrode, wherein the MOSFET includes an SiC-MOSFET provided in the semiconductor chip, the source region is formed utilizing the emitter region of the SiC-IGBT, the drain region is formed adjacent to the collector region of the SiC-IGBT such that the drain region is selectively exposed on the second surface of the SiC semiconductor layer, the collector electrode is collectively connected to the drain region and the collector region, the SiC semiconductor layer includes: a second conductive-type SiC substrate defining the second surface of the SiC semiconductor layer and selectively formed with a trench from the second surface toward the first surface, and a second conductive-type SiC base layer formed on the SiC substrate to serve as the base region defining the first surface of the SiC semiconductor layer, wherein the drain region and the collector region are formed at the bottom surface of the trench in a manner adjacent to each other.
 8. A semiconductor device comprising: a semiconductor chip formed with an SiC-IGBT (Insulated Gate Bipolar Semiconductor) including: an SiC semiconductor layer having a first surface and a second surface, a first conductive-type collector region formed such that the collector region is exposed on the second surface of the SiC semiconductor layer, a second conductive-type base region formed closer to the first surface of the SiC semiconductor layer with respect to the collector region such that the base region is in contact with the collector region, a first conductive-type channel region formed closer to the first surface of the SiC semiconductor layer with respect to the base region such that the channel region is in contact with the base region, a second conductive-type emitter region formed closer to the first surface of the SiC semiconductor layer with respect to the channel region such that the emitter region is in contact with the channel region, the emitter region defining a portion of the first surface of the SiC semiconductor layer, a collector electrode formed such that the collector electrode is in contact with the second surface of the SiC semiconductor layer, the collector electrode connected to the collector region, and an emitter electrode formed such that the emitter electrode is in contact with the first surface of the SiC semiconductor layer, the emitter electrode connected to the emitter region; and a MOSFET (Metal Oxide Semiconductor Field Effect Transistor) connected in parallel to the SiC-IGBT, the MOSFET including: a second conductive-type source region electrically connected to the emitter electrode; and a second conductive-type drain region electrically connected to the collector electrode, wherein the MOSFET includes an SiC-MOSFET provided in the semiconductor chip, the source region is formed utilizing the emitter region of the SiC-IGBT, the drain region is formed adjacent to the collector region of the SiC-IGBT such that the drain region is selectively exposed on the second surface of the SiC semiconductor layer, the collector electrode is collectively connected to the drain region and the collector region, and the base region includes a drift region having a first impurity concentration in contact with the channel region and a buffer region formed such that the buffer region surrounds the collector region between the drift region and the collector region and having a second impurity concentration higher than the first impurity concentration.
 9. The semiconductor device according to claim 8, wherein the SiC semiconductor layer includes: a second conductive-type SiC substrate defining the second surface of the SiC semiconductor layer; and a second conductive-type SiC base layer formed on the SiC substrate to serve as the base region defining the first surface of the SiC semiconductor layer, wherein a trench penetrating from the second surface of the SiC substrate through the SiC substrate to reach the SiC base layer is selectively formed, and wherein the drain region is formed utilizing the SiC substrate, the collector region is formed at the bottom surface of the trench, and the SiC base layer includes: a second conductive-type buffer layer formed such that the buffer layer surrounds the collector region to serve as the buffer region; and a second conductive-type drift layer formed on the buffer layer to serve as the drift region.
 10. The semiconductor device according to claim 8, wherein the SiC semiconductor layer includes: an SiC substrate defining the second surface of the SiC semiconductor layer and having a first conductive-type portion and a second conductive-type portion segmented such that the first and second conductive-type portions are exposed separately on the second surface; and a second conductive-type SiC base layer formed on the SiC substrate to serve as the base region defining the first surface of the SiC semiconductor layer, and wherein the collector region is formed utilizing the first conductive-type portion of the SiC substrate, the drain region is formed utilizing the second conductive-type portion of the SiC substrate, and the SiC base layer includes: a second conductive-type buffer layer formed on the SiC substrate such that the buffer layer covers the drain region and the collector region to serve as the buffer region; and a second conductive-type drift layer formed on the buffer layer to serve as the drift region. 